Kristallstrukturuntersuchungen von Hauptgruppen-Nitriden mittels Pulverbeugung
Kristallstrukturuntersuchungen von Hauptgruppen-Nitriden mittels Pulverbeugung
In this thesis new nitrides and imides were investigated by powder diffraction methods. The crystal structures of a series of nitridophosphates and nitridocarbonates which were available only as powder were solved by direct methods after indexing and extraction of the integrated intensities. By neutron powder diffraction on the one hand hydrogen was localized in an imide, on the other hand the elements nitrogen and oxygen, which are difficult to distinguish by X-ray diffraction, were discerned in oxonitridophosphates and oxonitridosilicates. Thus the importance of the powder diffraction for nitrides could be proved., In der vorliegenden Arbeit wurden neue Nitride und Imide mit Pulverbeugungsmethoden untersucht. Die Kristallstrukturen einer Reihe von Nitridophosphaten und Nitridocarbonaten, die nur als Pulver vorlagen, wurden nach der Indizierung und dem Extrahieren der integrierten Intensitäten mit Direkten Methoden bestimmt. Mit Neutronenbeugung an Pulvern wurde einerseits Wasserstoff in einem Imid lokalisiert, andererseits die mit Röntgenbeugung schwer zu unterscheidenden Elemente N und O in Oxonitrophosphaten und Oxonitridosilicaten unterschieden. Damit konnte die Bedeutung der Pulverbeugung im Bereich der Nitride gezeigt werden.
Not available
Irran, Elisabeth
2001
Deutsch
Universitätsbibliothek der Ludwig-Maximilians-Universität München
Irran, Elisabeth (2001): Kristallstrukturuntersuchungen von Hauptgruppen-Nitriden mittels Pulverbeugung. Dissertation, LMU München: Fakultät für Chemie und Pharmazie
[thumbnail of Irran_Elisabeth.pdf]
Vorschau
PDF
Irran_Elisabeth.pdf

6MB

Abstract

In this thesis new nitrides and imides were investigated by powder diffraction methods. The crystal structures of a series of nitridophosphates and nitridocarbonates which were available only as powder were solved by direct methods after indexing and extraction of the integrated intensities. By neutron powder diffraction on the one hand hydrogen was localized in an imide, on the other hand the elements nitrogen and oxygen, which are difficult to distinguish by X-ray diffraction, were discerned in oxonitridophosphates and oxonitridosilicates. Thus the importance of the powder diffraction for nitrides could be proved.

Abstract

In der vorliegenden Arbeit wurden neue Nitride und Imide mit Pulverbeugungsmethoden untersucht. Die Kristallstrukturen einer Reihe von Nitridophosphaten und Nitridocarbonaten, die nur als Pulver vorlagen, wurden nach der Indizierung und dem Extrahieren der integrierten Intensitäten mit Direkten Methoden bestimmt. Mit Neutronenbeugung an Pulvern wurde einerseits Wasserstoff in einem Imid lokalisiert, andererseits die mit Röntgenbeugung schwer zu unterscheidenden Elemente N und O in Oxonitrophosphaten und Oxonitridosilicaten unterschieden. Damit konnte die Bedeutung der Pulverbeugung im Bereich der Nitride gezeigt werden.